TFC PU Casting Resin Resin 4 min 1:1

TFC PU Casting Resin is a high-quality, almost odourless two-component casting compound.
Suitable for moulds, master models, figures, core souls, negatives, control casts, sample parts, etc.

Properties and application:
- low odour
- simple mixing ratio 1:1 by weight
- very good flowability
- very high strength
- impact resistant after final hardening
- colour in final hardening: white to beige
- can be coloured with casting resin colours
- not UV-resistant
- can be processed (drilling, grinding, etc.) without any problems after final hardening.)
- forms a closed surface that can be painted and designed

Main areas of application
- production of moulds, models, core souls and tool parts in mould making and model making
- production of decorative objects for crafts and arts and crafts
- production of figures, dioramas, miniatures and small parts with particularly fine contours
- universal for moulds and models of all kinds


Further product information:
Colour: A whitish/beige and B beige
Mixture: 1:1 by weight
Specific weight: 1.00
Viscosity 55 mPas
Processing time (100g) at 25° Celsius 3-4 minutes
De-moulding time at 25° Celsius 75 minutes
Hardness Shore D 75
Heat resistant up to approx. 65-70 degrees° Celsius
Tensile strength 33 MPa
Tensile elongation 6%
Bending strength 33 MPa
E-modulus from bending test 650 MPa
Linear shrinkage approx. 0.15%

Processing instructions:
- Mix both components carefully and separately before use.
- Mix both components thoroughly at room temperature (> 18° C) according to the specified mixing ratio.
- Before casting, ensure that parts and moulds are free from moisture and non-dehumidified release agents.